Method and System For Generating a Photo-Response From MoS2 Schottky Junctions

ABSTRACT

Devices incorporating a single to a few-layer MoS 2  channels in combination with optimized substrate, dielectric, contact and electrode materials and configurations thereof, exhibit light emission, photoelectric effect, and superconductivity, respectively.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. application Ser. No. 13/661,979, filed Oct. 26, 2012, entitled “METHOD AND SYSTEM FOR GENERATING A PHOTO-RESPONSE FROM MoS₂ SCHOTTKY JUNCTIONS,” which claims benefit of priority to. U.S. Provisional Patent Application Nos. 61/552,914, filed Oct. 28, 2011, entitled “ELECTRONIC AND OPTOELECTRONIC DEVICES USING SINGLE LAYER MoS₂,” and 61/616,202, filed Mar. 27, 2012, entitled “METHOD AND SYSTEM FOR GENERATING A PHOTO-RESPONSE FROM MoS₂ SCHOTTKY JUNCTIONS,” all of which are incorporated herein by reference.

BACKGROUND

1. Field of the Embodiments

The embodiments described herein are generally directed to components incorporating molybdenum disulfide (MoS₂).

2. Description of the Related Art

MoS₂ is a semiconductor made of layers that are weakly coupled by van der Waals forces and can be easily separated via chemical or mechanical exfoliation to obtain few-layer or single-layer samples. A layer is made of three atomic planes that are strongly bonded to each other: two hexagonal planes of sulfur atoms separated by one hexagonal plane of molybdenum atoms, with each molybdenum atom covalently bonded to six sulfur atoms in the adjacent planes (see FIG. 1 a Layered structure of MoS₂, where X represents a S atom and T a Mo atom). Additional description may be found in A. Kuc et al., Influence of quantum confinement on the electronic structure of the transition metal sulfide TS(2), Physical Review B, 83 (2011) which is incorporated herein by reference. FIG. 1 b illustrates the effect of quantum confinement on the band structure of MoS₂.

Bulk MoS₂ is a semiconductor with an indirect bandgap of 1.2 eV. When the thickness is reduced to a few layers, the indirect bandgap is tuned by quantum confinement and increases by 0.5 eV or more, until it eventually exceeds the energy spacing of the direct gap for single-layer thickness, at about 1.9 eV. When varying the thickness, photoluminescence experiments have shown that the quantum yield increases by a few orders of magnitude for single-layer samples, confirming the crossover from indirect to direct gap. For a single layer, the quantum yield has also been found to be higher when the layer is suspended.

These results make single-layer MoS₂ a possible candidate for optoelectronics applications, as well as for other device applications where a large energy gap, a large surface area, and a high surface-to-volume ratio are crucial. Presently, the technological potential of this material still remains largely unexplored. Single-layer and few-layer transistors have been only recently realized by depositing thin flakes of MoS₂ on a doped silicon substrate capped with an insulating silicon dioxide layer. The MoS₂ thin flakes are first deposited using the same method that yielded the first successful single-layer graphene devices, i.e. mechanical exfoliation with scotch tape, then attachment of gold source and drain electrodes across the MoS₂ layer. The number of layers can be roughly sorted by contrast imaging with an optical microscope, whereas accurate measurements are obtained either by Raman spectroscopy or by AFM measurements of the thickness, which is about 0.65 nm for a single layer. In some devices, top gates with a different material for gate dielectric are also deposited (see FIG. 2 a). Electrical characterization of the device is shown in FIG. 2 b. The performance of MoS₂ devices has been found to vary greatly depending on the gate dielectric material. For example, HfO₂ gate oxide on single layer flakes yielded on-off current ratio as high as 1×10⁸ and mobility higher than 200 cm²V⁻s⁻¹ at room temperature. These first results show that transistors can be obtained.

There is a need in the art to advantageously implement MoS₂ in various processes and devices to improvements in light emitting devices, photoelectric devices, superconductivity and the like.

SUMMARY

In a first exemplary embodiment, a solid-state device includes: a channel formed of a single-layer of MoS₂ on a substrate; and a source contact formed of at least a first material and a drain contact formed of at least a second material on the substrate and in contact with first and second ends of the channel, wherein Schottky junctions are formed at an interface of at least one of the source and drain contacts and the channel exhibiting a photovoltaic effect.

In a second exemplary embodiment a solid-state light emitting device includes: a channel formed of a single-layer of MoS₂ on a substrate; a source contact formed of at least a first material and a drain contact formed of at least a second material on the substrate and in contact with the channel; a dielectric layer formed on the single-layer of MoS₂ and the source and drain contacts; and first and second gate electrodes formed on the dielectric layer.

BRIEF DESCRIPTION OF THE FIGURES

The following figures exemplify the embodiments described herein and are intended to be reviewed in combination with the detailed descriptions provided below.

FIGS. 1 a and 1 b illustrate the known structure of MoS₂ and characteristics thereof;

FIGS. 2 a and 2 b illustrate a prior art single layer MoS₂ transistor and characteristics thereof;

FIG. 3 a shows a MoS₂ transistor with Au contacts, resulting in only n-type behavior and FIG. 3 b shows a MoS₂ transistor with Pd contacts resulting in only p-type behavior;

FIGS. 4 a-4 d illustrate MoS₂ transistor with varying electrode materials and band alignment characteristics thereof;

FIG. 5 a-5 c illustrates contact potential difference (CPD) between two dissimilar metals;

FIGS. 6 a and 6 b illustrate exemplary device testing structure and CPD measured at various times;

FIGS. 7 a-7 e illustrate: (a) Optical image of the device. The spacing between the electrodes is 2 μm. (b) Connections for source-drain bias and for gate-drain bias. (c) and (d) Transfer characteristics and photoresponse for a device with Pd—Au electrodes, for positive (c) and negative (d) source-drain bias. (e) Current vs. source-drain voltage showing strong asymmetry and photoresponse with diode-like behavior;

FIGS. 8 a and 8 b illustrate device in accordance with preferred embodiment and pn junction and light emission due to electron-hole recombination

FIGS. 9 a-9 c illustrate: a) Calculated band structure of single layer MoS₂; b) parabolic fits to the bottom of the conduction band and top of the valence band and c) phonon spectrum, with Raman-active modes marked; and

FIG. 10 illustrates Fermi surface with doping of electrons with in-plane versus out-of-plane character of the states.

DETAILED DESCRIPTION

Ambipolar MoS₂ transistors with Au source-drain contacts were very recently demonstrated, but they were gated with ionic liquids (electrolytic gate) and the mechanism that leads to ambipolar transport in these samples is still unclear. By contrast, embodiments described and optimized through process discussed herein are all-solid-state devices that show either n-type or p-type transistor behavior, depending on the, choice of electrode material. It has been found that when source and drain contacts are made of palladium (Pd), MoS₂ transistors always show p-type behavior. Devices made with two different contacts, Au and Pd, show asymmetric ambipolar behavior and diode characteristics in a wide range of gate voltages. These results can be explained assuming different work functions for Pd, MoS₂ and Au. The sizable photovoltaic effect measured within these devices is thought to arise from the built-in potential of the space charge accumulated at the source-drain contacts.

In a first embodiment, samples are made of exfoliated multi- and few-layer flakes of MoS₂ (about 50 nm thick) on a doped Si substrate capped with 300 nm SiO₂. Additional substrate materials may include glass, as well as flexible materials discussed below. Source and drain electrodes are patterned by e-beam lithography and deposited by sputtering. FIGS. 3 a and 3 b shows the transfer characteristics of two typical samples. In the case of Cr (2 nm)/Au (100 nm) source and drain electrodes, the device exhibits n-type behavior, similar to devices previously reported (FIG. 3 a). Here we find that even extending the measurements to a very wide range of gate voltage, −100 V<VG<100 V, about 10 times wider than measurements previously reported, no p-type conduction can be measured. However, remarkably, in the case of Nb (2 nm)/Pd (100 nm) electrodes (FIG. 3 b), the behavior is reversed and the sample shows only p-type conduction in the same range of gate voltage.

The reversed polarity is explained by assuming that 1) the thin adhesion layers of Cr and Nb can be neglected, since their thickness is too small to obtain a uniform film (that is, the adhesion layer is made of small disconnected islands or patches of metal) and the contact to the source and drain electrode is, mainly made by the thick Pd and Au layers and 2) (φPd>φMoS2>φAu, as shown schematically in FIG. 4 a, 4 b, where φ is the work function of each material. This will cause doping of the MoS₂ channel and accumulation of space charge in the contact region, yielding Schottky barriers and either upward (hole doping) or downward (electron doping) bending of the conduction and valence band edges.

In the case of electron-doping Au contacts (FIG. 4 a), when a positive gate voltage is applied, the bands shift downward, the curvature of the band profile is reversed and the Schottky barrier becomes thinner, yielding higher tunneling current through the conduction band. For negative gate voltages, the bands shift upward, the curvature of the band profile increases and large barriers at the contacts block the source-drain current through the valence band. An analogous picture can explain the p-type transfer characteristics of the Pd devices, assuming that the situation for Pd contacts is just the opposite.

Although the literature values for the Au and Pd work functions are very similar, chemical interactions and charge redistribution at the interfaces change the alignment of Fermi levels for the. Au/MoS₂ and the Pd/MoS₂ interfaces consistently with the scenario sketched in FIG. 4. This is also confirmed by our Kelvin probe measurements of Au and Pd work functions.

A Kelvin probe measurement tool (KP Technology—Wick, Scotland) uses the principle of a vibrating capacitor to determine work function of a metal, φ. The technique determines the contact potential difference (CPD) between two dissimilar metals that are electrically connected to each other. With the two metals initially unconnected but under the same ambient condition (FIG. 5 a), their vacuum levels align and their work functions will determine the difference in their Fermi levels. If the two metals are then electrically connected by a conducting wire, electrons will flow from the metal with the smaller work function, giving it a net positive charge, to that of the larger, which becomes negatively charged (FIG. 5 b). This is a self-limiting process since electron transfer becomes impeded by the resulting electric field generated by the potential difference between the two metals, which at equilibrium, is exactly the work function difference, designated as the CPD. With the careful application of an external DC voltage to the capacitive circuit, the effect of the CPD can be counteracted to effectively produce a null potential difference (FIG. 5 c).

In the actual Kelvin probe tool, one of the metals forms a suspended probe above the second sample metal under test, effectively forming a variable capacitor. The probe is actuated at a set frequency that generates a sinusoidal variation in current response, thereby allowing the capacitor to go through a charge/discharge cycle. The counterbalancing DC voltage is ramped from a negative to positive potential, and by plotting the IV curve, a zero value for AC current can be interpolated to determine the CPD.

The Kelvin probe system is used to measure the work function of both gold and palladium (Pd) with respect to the stainless steel probe in two different states: one is to perform the measurement in air immediately after sputter deposition, while the second is after both samples have been in air for 8 days (FIGS. 6 a and 6 b). In FIG. 6 a, the tested device is a 20 mm×20 mm×500 nm sample, half Pd and half Au, sputtered on a Si/SiO₂ substrate. It has been determined that the work function of Pd is indeed higher than the work function of Au right after sputtering, but their difference decreases after exposure to air.

The effect of the electrode material on MoS₂ was determined by using two Pd electrodes and one Au electrode on the same MoS₂ flake, as shown in FIG. 7 a. When the Au contact is used as the drain electrode and either one of the Pd contacts is used as the source electrode, both p-type and n-type behavior can be measured, although the on-state current in the valence band is about one order of magnitude higher than the on-state current in the conduction band (FIG. 7 b). The transfer characteristics measured at equal and opposite values of source-drain voltage, VSD, reveal a strongly asymmetric, diode-like behavior as a function of source-drain bias (FIG. 7 c, 7(d). The corresponding current- vs. source-drain voltage (IV) curves also show diode-like behavior and photoresponse, when irradiated with a laser having photon energy larger than the gap (532 nm laser, photon energy about 2.3 eV, intensity, of 1 mW/mm²).

These results may be explained considering that the built-in Schottky potential at the Au/MoS₂ and the Pd/MoS₂ interfaces separates the electrons and holes generated by the absorbed photons and accumulates them at the electrodes, yielding an open-circuit voltage V_(OC)=0.1 V, as shown by the laser ON curve in FIG. 7 e. This work is the first demonstration of photovoltaic effect from MoS₂ flakes. Additional details related to the electrode study are described in similarly titled U.S. Provisional Patent Application Ser. No. 61/616,202 to which the present application claims benefit of priority and which is incorporated herein by reference in its entirety.

In accordance with the embodiments described in U.S. Provisional Patent Application Ser. No. 61/616,202, it is estimated that the maximum electrical power that can be extracted from the device is about 2.5% of the laser power incident on the MoS₂ region between the electrodes. This percentage is a lower bound for the conversion efficiency, because only the depletion region in the MoS₂ channel is photoactive. Nevertheless, this room-temperature efficiency is better than the highest value previously reported in MoS₂, which was about 1% at 120 K for bulk samples.

The following variations to the devices described and illustrated herein are expected to enhance the photovoltaic effect and improve device characteristics.

In a first variation, the device as illustrated in FIG. 7 b is fabricated using MoS₂ flakes formed with multiple layers. Though an increase in conversion efficiency would be expected when the energy gap goes from indirect to direct as the number of layers is decrease, recent work has predicted that reducing the thickness to a single layer could lead to significant excitonic effects due to reduced screening in 2-dimensionals, thereby hindering the electron-hole separation that is essential for the photovoltaic effect. Accordingly, multiple layer flakes may result in a balance of physical attributes that improves electron-hole separation while avoiding deleterious effects of increasing number of layers comprising the MoS₂ flakes.

In a second variation, the device as illustrated in FIG. 7 b is fabricated wherein the spacing of the metallic electrodes forming the Schottky barriers with the MoS₂ will be varied, on the same flake. It is expected that as the distance between those electrodes becomes shorter than the electron-hole recombination length that the conversion efficiency will increase. Additional variations include fabrication of devices having sections of the MoS₂ flakes connected in series and in parallel with alternating Au/Pd electrodes, to create arrays of photodiodes with increased total open-circuit voltage and closed-circuit current, respectively.

In a third variation, the device as illustrated in FIG. 7 b is fabricated using MoS₂ flakes with Au/Pd electrodes on flexible polymer substrates, such as polyimide or polydimethylsiloxane (PDMS), to test how the photovoltaic effect is affected by bending of the flexible substrate.

In a fourth variation, the device as illustrated in FIG. 7 b is fabricated using MoS₂ flakes with Au/Pd electrodes as discussed here on substrates with reflective coating, to recycle photons that are not absorbed or are generated by recombination of electron-hole pairs into the creation of new pairs. Such a reflective surface is expected to increase photovoltaic efficiency. The reflective surface may be metallic including, but not limited to, Au, Al, Ag, Pt and/or multi-layer dielectric reflective films including, but not limited to, TiO₂, SiO₂, Al₂O₃, Ta₂O₃.

Returning to the single layer embodiment, FIGS. 8 a and 8 b illustrate a system wherein a pn junction is made by electrostatic doping of a single layer of MoS₂. Per above, the embodiments show ambipolar transport can be obtained in multilayer flakes. FIGS. 8 a and 8 b illustrate ambipolar transport in single-layer MoS₂ which allows for formation of pn junctions and the fabrication of nanoscale light sources.

In FIG. 8 a a single layer of MoS₂ is deposited on a doped Si substrate which is capped with an insulating layer, e.g. SiO₂. Source and drain electrodes will be then deposited to contact the MoS₂ layer. The materials for source and drain are Pd and Au, respectively to provide local doping of opposite polarity at the interfaces between the electrodes and the MoS₂. A dielectric layer is grown by atomic layer deposition having a thickness in the range of 5 Angstroms to 100 nanometers and, as a final step, two separate gate electrodes are deposited on top of the structure. Initially, the transfer characteristic of the device as a function of the bottom gate is determined, to measure the ambipolar transport characteristics. The top gates are then biased with voltages of opposite sign to further shift the Fermi energy of the MoS₂ regions underneath them into the valence band and conduction band respectively, thereby obtaining a pn junction.

It is expected that light can be detected from the resulting pn junction. Forward biasing of this pn junction leads to electron-hole recombination in the junction region and emission of photons with energy matching the single-layer MoS₂ energy gap, 1.9 eV. Furthermore, radiative recombination of electron-hole pairs should be favored by the strong excitonic effects predicted in single-layer MoS₂. This light is in the visible portion of the electromagnetic spectrum and will be emitted from the gap separating the two top electrodes. The detector of a Raman Renishaw spectrometer may be used to measure the emitted light and its spectrum.

This type of light emitting pn junction, where the pn regions are obtained by electrostatic doping, has been already successfully used for carbon nanotubes. MoS₂ can be adapted to batch fabrication techniques much more easily than carbon nanotubes, which are not at all amenable to mass production. Accordingly, although to date MoS₂ devices are currently fabricated by mechanical exfoliation, it is anticipated that similar to graphene, methods to grow single layer MoS₂ on wafers will be developed.

Successful detection of light from MoS₂ pn junctions is extremely attractive for both applications as well as basic science. For example, shrinking the size of the light source by confining electrons and holes may lead to new types of lasers with no threshold and no need of high Q cavity. High confinement can be obtained by forming pn junctions from MoS₂ nanoribbons, so this type of device can be used to build nanoscale light sources and to study possible occurrence of coherent emission due to confinement of electrons and holes. Nanoscale lasers have been recently demonstrated using surface plasmon oscillations, as a first step towards the development of on-chip optical computing. However, nanolasers achieved to date can only be pumped optically, whereas on-chip light sources for optical interconnects require electrical pumping, making MoS₂ light sources extremely desirable. In addition, arrays of light sources could be easily fabricated from MoS₂ layers.

There are still many open basic questions on transport properties of MoS₂, including the origin of the large hysteresis observed in most devices and whether it can be controlled or reduced, the contribution to the resistance due to the contact versus the scattering in the MoS₂ layers and the dependence of these contributions on the number of layers. Regarding scattering within few-layers or single-layer MoS₂, it is not clear whether ballistic transport can be achieved in these systems and what is the role played by the substrate and therefore the roughness of the gate oxide. However, zero resistance due to superconductivity has been measured in MoS₂ intercalated with sodium and potassium yielding critical temperatures of a few. Kelvin. Recently superconductivity has also been measured in thin MoS₂ flakes doped with an electrolytic gate, with critical temperatures up to 9 K. The authors find that superconductivity occurs only in a narrow region of gate voltage where the Fermi energy is shifted within the conduction band. These measurements suggest that the onset of superconductivity is related to the increase in charge carrier density. Superconductivity due to hole-doping, however, has not been reported. The following systems and processes are implemented to determine the transport properties of MoS₂ flakes, including the onset of field-effect superconductivity and its dependence on the doping, the number of layers, and quantum confinement obtained by cutting MoS₂ flakes into nanoribbons.

Initially, for both single- and few-layer MoS₂ flakes, electrodes are deposited with increasing spacing on the same flake to extract the contact resistance as well as the sheet resistance of the flake and its temperature dependence. This process is repeated for different electrode materials to find the material that provides the best contact to the flakes.

The influence of the substrate is determined by measuring the sheet resistance of flakes on different dielectric substrates deposited by atomic layer deposition, to investigate the effect of electron-phonon scattering and of the substrate on transport properties. Different dielectric layers are deposited by atomic layer deposition, including HfO₂ and Al₂O₃, and results studied. More particularly, characterization of the roughness of the layer and its effect on the MoS₂ transport properties is determined.

The onset of superconductivity in gated MoS₂ devices is determined by measuring the resistance as a function of temperature. The source-drain electrode material determined to provide the best contact to the MoS₂ is utilized. In the case of Pd electrodes, fully solid state devices are achieved where hole transport can be measured. These devices are cooled to low temperature (2.5 K) and the gate is continuously scanned to shift the Fermi energy in the valence band and detect superconductivity in the hole-doping regions. This allows for differential study of the gate dependence of the superconducting properties when compared to samples with prior art electrolytic gate. This is because the electrolytic gate freezes at the low temperatures required to measure superconductivity, therefore the sample needs to be warmed up in order to effectively change the gate and the (electrically induced) doping, making a fine tuning of the gate very time consuming when using an electrolytic gate.

Additionally, superconductivity in suspended and gated MoS₂ flakes is determined. In suspended structures, electrons may couple to different phonon modes, yielding a different critical temperature.

Further, the MoS₂ flakes are cut in the shape of nanoribbons, to obtain a density of states with one-dimensional subbands and sharp van Hove singularities at the onset of each subband. The doping dependence of the superconducting properties is expected to be substantially different and yield higher critical temperatures. This is expected because the density of states increases dramatically when the Fermi energy is shifted into a van Hove singularity by applying a gate voltage to a nearby gate electrode. The nanoribbons are patterned by e-beam lithography and masking a narrow stripe of MoS₂ with PMMA prior to dry etching.

In recent prior art investigations of superconductivity in isolated carbon nanotubes in the field effect transistor configuration, an applied gate voltage can be used to shift the Fermi energy into van Hove singularities of the density of states, yielding transport features that can be interpreted as signatures of superconductivity, with critical temperature higher than 25 K for some samples. In single carbon nanotube devices, Andreev reflection at the contacts as well as thermal and quantum fluctuations strongly affect the temperature dependence of the resistance and cause a resistive tail below the critical temperature. The transition is expected to get much sharper when multiple nanotubes are coupled together. However, since the spacing of van Hove singularities depends on the carbon nanotube diameter and the nanotube diameter cannot be easily controlled, when samples are made with multiple nanotubes it is very difficult to shift the Fermi energy into van Hove singularities for all the nanotubes and optimize the critical temperature. As a result, reported critical temperatures of samples with multiple nanotubes have always much lower than 25 K, but the superconducting transition was sharper. It has been argued that ropes are different from a system of uncoupled 1D conductors, because Cooper pairs can hop even between tubes of different helicity. In the case of few-layer MoS₂ nanoribbons, each layer can be considered as a 1D conductor coupled to the adjacent layers. These layers will have the same width, therefore the same spacing of van Hove singularities. Accordingly, it is possible to shift the Fermi energy into van Hove singularities for all the layers with a common gate voltage and achieve critical temperature higher than the 9 K critical temperature recently reported for electrolytic gated MoS₂.

Processes described herein include optimization of devices for achieving superconductivity in single and/or few-layer MoS₂ devices through investigation of interface properties and charge scattering mechanisms, considering both electron and hole conduction. More particularly, investigative processes seek to improve electron mobilities and determine how to achieve and enhance hole conduction. In the prior art, for n-type conduction in single-layer MoS₂, mobilities of less than 10 cm²V⁻¹s⁻¹ were originally reported. The enhancement to 200 cm²V⁻¹s⁻¹ in the presence of the HfO₂ top gate as reported in the prior art is likely due to a reduction in impurity scattering by dielectric screening, though substrate-induced changes in the phonon properties could also reduce scattering of charge carriers.

Recent prior art density-functional-theory (DFT) calculations of the intrinsic electron-phonon scattering mechanisms in n-type single-layer MoS₂ report an estimate of about 400 cm²V⁻¹s⁻¹ as the upper bound on the mobility. Present process embodiments assess mobility in the valence band to see whether the intrinsic limits on hole transport are more stringent. While the effective masses at the conduction band minimum and the valence band maximum in single-layer MoS₂ are calculated to be similar (see FIGS. 9 a and 9 b), with m_(c)*˜0.5 m_(c) and m_(v)*˜0.5 m_(e) to 0.75 m_(e), the electron and hole states differ in character. The conduction band minimum at the K point is primarily of Mo d_(z) ² character while the valence band maximum at K is mainly derived from in-plane d states. The interaction of electrons with phonons can therefore be very, different depending on whether the carrier is in the conduction or valence band, leading to different mobilities. In addition to the intrinsic electron and hole mobilities, the effect of the substrate on phonon scattering in MoS₂ is also considered.

The mobility optimization in nanoscale systems contemplated the choice of contact material as well as the channel material in determining the electronic and transport properties of the system. Recent prior art computational studies of the electronic structure of single-layer MoS₂ in contact with various metals suggests that the most commonly used contact material, gold, may not be optimal, and that this may explain, in part, why conduction-band mobilities have not been as large as expected. Titanium was suggested as a better choice, given that the MoS₂/Ti interface has a high density of delocalized states at the Fermi energy. Optimization hereby includes determining compatibility in terms of atomic structure as well as electronic structure at the interface, and also determining Schottky barriers. An optimal contact material is identified to enhance p-type transport and to optimize the built-in potential necessary for separating charge in the photovoltaic effect.

With regard to attaining superconductivity in MoS₂, an initial step is examination of the phonon spectrum calculated for a single layer of MoS₂ as shown in FIG. 9 c. The Raman-active modes at the zone center are in good agreement with recent measurements. In a single-layer MoS₂ electrochemically gated field-effect transistor, these two Raman-active modes have been shown to respond very differently to electron doping. While the E_(2g) mode is relatively insensitive to doping, the A_(1g) mode softens and broadens considerably, suggesting a strong electron-phonon interaction. Indeed, DFT calculations confirm that the A_(1g) phonon, which involves out-of-plane displacements of S ions, interacts strongly with the Mo d_(z) ² states at the conduction band minimum, which renormalizes the phonon frequency due to enhanced screening. On the other hand, by symmetry, the E_(2g) mode does not couple (to lowest order) to the states at the bottom of the conduction band, which explains its inertness with respect to electron doping.

Next, the process looks to determine whether the strong coupling, of the A_(1g) mode to electrons in the conduction band can also explain the superconductivity observed in electrolytically gated devices made of thin MoS₂ flakes. FIG. 10 shows the Fermi surface calculated for a single-layer of MoS₂ doped with 0.06 electrons per formula unit, corresponding to a carrier density of about n=6×10¹³ cm⁻². For comparison, in the prior art (Chakraborty et al., Symmetry-dependent phonon renormalization in monolayer MoS₂ transistor, Physical Review B, 85 (2012) which is incorporated by reference herein), a gate voltage of 2 eV is estimated to yield carrier densities around 2×10¹³ cm⁻². The Fermi surface of FIG. 10 shows that both the valley at K and the valley located about halfway between Γ and K are occupied. Unlike the conduction band, minimum at K, the ½ (ΓK) valley consists of states with a strong mix of in-plane Mo d and in-plane S p character. For electron-phonon mediated superconductivity, interest is in phonons that couple states on the Fermi surface.

Current results show strong contributions to the electron-phonon coupling parameter from intervalley phonon wave vectors Q=M and Q′=K. While the optical A_(1g) mode gives a large contribution at the zone center, corresponding to intrasheet coupling (Q=Γ), for Q=M and K, acoustic modes involving in-plane Mo motion and in-plane or out-of-plane S motion provide the largest contributions to the coupling constant. Although the coupling constant λ_(Q) is large at and near these wave vectors, the phase space over which the coupling is non-zero is limited by the small size of the Fermi sheets. Nevertheless, for electron doping of 0.06 electrons per formula unit, we estimate a total coupling constant of λ˜0.9. This is consistent with a superconducting T_(c) on the order of a few K. For comparison, the, potassium intercalated bulk material K_(x)MoS₂ has a peak T_(c) of about 7 K when x=0.4, while electron-doped liquid-gated few-layer MoS₂ devices have been reported to show superconductivity around 9 K. The carrier density in the latter case is still unclear.

Since the location and character of the hole sheets of the Fermi surface are very different from those of the electron sheets, it is expected that different phonon modes will be important for superconductivity in the hole-doped case. In both the hole-doped and electron-doped cases, optimization includes the examination of the effect of carrier concentration, strain, number of layers, interlayer interactions, and further reduction of dimensionality (i.e., nanoribbons) on electronic structure, vibrational properties, electron-phonon coupling, and superconductivity. For example, in the electron-doped case, when the doping level is sufficient to start occupying the ½ (ΓK) valleys, there should be a significant enhancement in superconductivity. Implementing methods, to preferentially increase the density of states in these valleys, and to increase the size of the associated Fermi sheets, enlarges the phase space of phonons that couple these sheets. To make contact with the proposed nanoribbon, structures that are neither perfect armchair nor perfect zigzag ribbons may be considered.

One skilled in the art recognizes that there are variations to the configurations and optimization processes discussed herein. Those variations are considered to be within the skill in the art and the scope, of the invention. 

We claim:
 1. A process for forming a solid-state device including at least one channel capable of exhibiting a photovoltaic effect comprising: forming a channel comprising a single-layer of MoS₂ on a substrate; and forming source contact comprised of at least a first material and a drain contact formed of at least a second material on the substrate and in contact with first and second ends of the channel, wherein Schottky junctions are formed at an interface of at least one of the source and drain contacts and the channel exhibiting a photovoltaic effect and further wherein the at least a first material and the at least a second material are different materials.
 2. The process of claim 1, wherein forming the source contact further includes forming a first adhesion layer on the substrate and depositing the at least a first material on the first adhesion layer.
 3. The process of claim 2, wherein forming the drain contact further includes forming a second adhesion layer on the substrate and depositing the at least one second material on the second adhesion layer.
 4. The process of claim 2, wherein the first material is palladium and the first adhesion layer is niobium.
 5. The process of claim 3, wherein the second material is gold and the second adhesion layer is chromium or titanium.
 6. The process of claim 1, wherein the substrate is formed of a flexible polymer.
 7. The process of claim 1, further comprising forming a reflective material on the substrate prior to forming the single-layer of MoS₂ on the substrate, wherein the reflective material is formed between the single-layer of MoS₂ and the substrate.
 8. The process of claim 1, further comprising forming the source contact and the drain contact such that a distance therebetween is shorter than an electron-hole recombination length of the device.
 9. The process of claim 1, further comprising forming multiple individual photovoltaic devices on the substrate, each of the multiple individual photovoltaic devices including a single-layer of MoS₂ and a single source contact and a single drain contact.
 10. The process of claim 9, further comprising connecting the multiple individual photovoltaic devices in series.
 11. The process of claim 9, further comprising connecting the multiple individual photovoltaic devices in parallel.
 12. The process of claim 9, further comprising connecting a first subgroup of the multiple individual photovoltaic devices in parallel and a second subgroup of the multiple individual photovoltaic devices in series.
 13. The process of claim 1, wherein forming the channel comprises exfoliating flakes of MoS₂ onto doped silicon (Si).
 14. A process for forming solid-state light emitting device comprising: forming a channel, comprising a single-layer of MoS₂ on a substrate; forming a source contact of at least a first material and a drain contact of at least a second material on the substrate and in contact with the channel, wherein the first material and the second material are different materials; forming a dielectric layer on the single-layer of MoS₂ and the source and drain contacts; and forming first and second gate electrodes on the dielectric layer.
 15. The process of claim 14, wherein forming the source contact further includes forming a first adhesion layer on the substrate and depositing the at least a first material on the first adhesion layer.
 16. The process of claim 15, wherein forming the drain contact further includes forming a second adhesion layer on the substrate and depositing the at least one second material on the second adhesion layer.
 17. The process of claim 15, wherein the first material is palladium and the first adhesion layer is niobium.
 18. The process of claim 16, wherein the second material is gold and the second adhesion layer is chromium or titanium.
 19. The process of claim 14, wherein the dielectric material is formed to a thickness in the range of 5 Angstroms to 100 nanometers.
 20. The process of claim 14, wherein forming the channel comprises exfoliating flakes of MoS₂ onto doped silicon (Si).
 21. The process of claim 14, further comprising biasing the first and second gate electrodes with opposite voltages.
 22. A nanoscale light source comprising, on a substrate: a single layer of MoS₂; a source electrode formed of a first material and located at a first end of the single layer of MoS₂; a drain electrode formed of a second material, different from the first material, and located at a second end of the single layer of MoS₂, wherein a gap is formed in the single layer of MoS₂ between the source electrode and the drain electrode; a dielectric layer formed on the single layer of MoS₂, the source electrode and the drain electrode; and first and second gate electrodes formed on the dielectric layer and biased with voltages of opposite sign, wherein a pn junction is formed in the gap and light is emitted therefrom in response to biasing the pn junction.
 23. The light source of claim 22, wherein the source contact further includes a first adhesion layer.
 24. The light source of claim 23, wherein the drain contact further includes a second adhesion layer.
 25. The light source of claim 24, wherein the first material is palladium and the first adhesion layer is niobium.
 26. The light source of claim 25, wherein the second material is gold and the second adhesion layer is chromium or titanium.
 27. The light source of claim 26, wherein the dielectric material has a thickness in the range of 5 Angstroms to 100 nanometers.
 28. The device of claim 27, wherein the substrate is doped silicon.
 29. A nanoscale light source comprising, on a substrate: a nanoribbon formed of a single layer of MoS₂; and a pn junction formed in the nanoribbon via electrostatic doping, wherein light is emitted therefrom in response to biasing the pn junction.
 30. The nanoscale light source of claim 29, wherein the pn junction is formed in a gap between a source electrode and a drain electrode formed on the nanoribbon.
 31. The nanoscale light source of claim 30, wherein the source electrode and the drain electrode are formed of different materials.
 32. The nanoscale light source of claim 31, wherein the different materials are selected from the group consisting of gold, palladium and titanium. 